Name | Aluminum Alloy Ingot ADC12 |
---|---|
Secondary Or Not | Non-secondary |
Alloy Or Not | Is Alloy |
Purity | 99.5% 99.7% 99.85% 99% |
Certificate | ISO |
Name | Aluminum Alloy Ingot ADC12 |
---|---|
Liquidus | 582 °C |
Melting Point | 516 – 582 °C |
Electrical Resistivity | 0.00000750 Ohm-cm |
Sample | Free |
Name | Aluminum Al Ingot |
---|---|
Aluminum, Al | 77.3 – 86.5 % |
Sample | Free |
Electrical Resistivity | 0.00000750 Ohm-cm |
Appearance | White |
Name | A383 Aluminum-Alloy |
---|---|
Appearance | Silvery White |
Hardness, Knoop | 109 |
Hardness, Vickers | 96 |
Fatigue Strength | 140MPA |
Name | Aluminum Alloy Metal Ingots |
---|---|
Chemical Composition | Al Cu Si Mg Zn Fe Mn Ni Sn |
Weight | 20kgs-25kgs |
Surface | Mill Finish, Smooth, Clean |
Appearance | Silvery White |
Appearance | Silvery White |
---|---|
Weight | 20kgs-25kgs |
Secondary Or Not | Non-secondary, Is Secondary |
Alloy | 1050, 2024, 3003, 5005, 5052, 5083, 6061, 7075, Etc. |
Grade | 1000 Series, Other, AA, Al & Other Metal, All |
Name | 99.7% Adc 12 Aluminium Ingot |
---|---|
Grade1000 Series, Other, AA, Al & Other Metal, All | 6000 Series |
Secondary Or Not | Non-secondary |
Al (Min) | 98% |
Weight | 20kgs-25kgs |
Name | Aluminum Alloy Ingot ADC12 |
---|---|
Electrical Resistivity | 0.00000750 Ohm-cm |
Secondary Or Not | Non-secondary, Is Secondary |
Melting Point | 516 – 582 °C |
Appearance | Silvery White |
Name | Aluminum Alloy Ingot |
---|---|
Appearance | Silvery White |
Density | 2.823 G/cc |
Elongation At Break | 2.5 % |
Grade | Adc 12 |
Appearance | Silvery White,clean |
---|---|
Grade | ADC 12 |
Delivery Port | Shanghai Port |
Machinability | 50 % |
Origin | China |